Composite tool

ABSTRACT

The invention relates to a composite tool consisting of a metallic supporting part and at least one such working part of different material compositions, which parts are metallically bonded to each other, in particular, a saw blade or bandsaw. For increasing the cutting yield and tool service life, in particular, when working titanium and titanium alloys, austenitic Cr—Ni—Mn—N steels and nickel and nickel-based alloys, the invention provides that the supporting part or the supporting strip are formed of a tenacious iron-based material and that the working part(s) are formed of a precipitation hardenable iron-cobalt-tungsten alloy (Fe—Co—W).

[0001] The invention relates to a composite tool comprising a metallic supporting part and at least one such working part of different material compositions, which parts are metallically joined together, in particular a saw blade or a bandsaw.

[0002] Tools on which the highest demands are made regarding the working part and the holding part or clamping part are usually made of different materials, with the respective material being selected to be the best possible for the strains on the part.

[0003] It is known to make saw blades or bandsaws out of a so-called bimetal strip, which strip is formed of a tenacious supporting part and a cutting part. While the supporting part is made of an alloy that ensures high elasticity, toughness, fracture-resistance and the like properties, the cutting part, which ultimately forms the cutting tooth tips, features a high material hardness, abrasion resistance and a like wear-resistance. Such saws have been part of the prior art for a long time, and the cutting part, formed, e.g., of high-speed steel, may be metallically bonded to the carrying or supporting part by welding. If, according to another possibility, the cutting tips are made of special materials, e.g., hard metal, they are to be bonded to the supporting part individually, in particular by brazing.

[0004] In the cutting of materials, the hardness, toughness and abrasion resistance of the tool blade usually determine the service life thereof in practical use. Hard material coatings are also often provided in the blade area of the tools in order to increase their cutting yields.

[0005] However, the cutting yield of cutting tools depends not only on the hardness of the blades and their abrasion resistance and toughness, but is also considerably influenced by the properties of the material to be cut. For instance, titanium, austenitic steels, nickel-based alloys and the like are known as materials that are difficult to cut. In a treatment of the above materials, it is often only possible to achieve low cutting yields with extremely high tool wear, even with high quality high-speed steels and hard metals. Roundnesses and craters in the blade area are usually the cause of the failure of the tool.

[0006] The invention is intended to remedy this situation, the object being to disclose a composite tool that has improved cutting properties of the working part. It is, in particular, the object of the invention to provide a tool for cutting titanium and titanium alloys, austenitic steels, nickel- and cobalt-based alloys and the like.

[0007] These objects are attained with a composite tool of the type mentioned at the outset in that the supporting part or the supporting strip is made of a tenacious iron-based material and the working part(s) are made of a precipitation hardenable iron-cobalt-tungsten alloy (Fe—Co—W). It has been found that tungsten can be replaced at least in part by molybdenum, and that improved cutting yields may possibly be achieved with iron-cobalt-tungsten plus molybdenum alloys (Fe—Co—W+Mo).

[0008] The advantages achieved with the invention can be seen essentially in that high cutting yields with considerably improved service life of the tool blade are possible even in austenitic steels, titanium- and nickel—as well as cobalt-based alloys. Here, the working part is advantageously bonded to the supporting part of the tool metallically, preferably by additive-free welding. It has not yet been scientifically determined why a precipitation-hardened iron-cobalt-tungsten alloy can particularly efficiently be effective in cutting materials that are known to be difficult to work on, e.g., Cr—Ni steel with more than 18% by weight of Cr and more than 10% by weight of nickel, which steel may additionally be alloyed with molybdenum, nitrogen and further elements. Initial studies indicate that a chip formation and a chip flow have a favorable effect by reducing the frictional forces while intensifying the tearing and shearing work.

[0009] High cutting yields of the tool can be achieved when the working part(s) has a composition in % by weight of Cobalt (Co) 15 to 30 Tungsten (W) up to 25 Molybdenum (Mo) up to 20 (W + Mo) 10 to 25 Silicon (Si) up to 1.5 Aluminum (Al) up to 1.5 Vanadium (V) up to 1.5 Titanium (Ti) up to 1.0 Niobium/Tantalum (Nb, Ta) up to 1.1 Carbon (C) a maximum of 0.4 Chromium (Cr) a maximum of 3.9 Nickel (Ni) a maximum of 3.9 Manganese (Mn) a maximum of 4.1

[0010] the balance being iron (Fe) and impurities caused by production. In the above alloying range the material properties regarding material hardness, toughness and abrasion resistance can be adjusted in a favorable manner by a heat treatment and the precipitation hardening effect, respectively, without adversely affecting the welding behavior of the working part and the connection with the supporting part, respectively.

[0011] Particularly high cutting yields with low tool wear can be achieved when the working part(s) has/have a composition in % by weight of Co 22 to 26, preferably 21 to 24 W up to 20, preferably 9 to 18 Mo up to 12, preferably 1 to 9 (W + Mo) 11 to 20 Si up to 0.8, preferably up to 0.6 Al up to 0.8, preferably up to 0.4 V up to 1.0, preferably 0.4 to 0.8 Ti up to 0.6, preferably up to 0.3 Nb/Ta up to 0.7, preferably up to 0.25 C a maximum of 0.2, preferably a maximum of 0.15 Cr a maximum of 0.9, preferably a maximum of 0.5 Ni a maximum of 0.8, preferably a maximum of 0.3 Mn a maximum of 0.9, preferably a maximum of 0.4

[0012] the balance being Fe and impurities caused by production.

[0013] As has been found, the preferred ranges of the material composition can be favorably used for the working part when cutting austenitic work pieces.

[0014] In order to achieve improvements regarding good performance qualities of the tool per se, it can be favorable if the supporting part is made of a carbon spring steel consisting of, in % by weight,

[0015] 0.25 to 1.15 C

[0016] 0.20 to 3.0 Si

[0017] 0.45 to 2.5 Mn

[0018] as well as Cr, V, Mo, Ni and S, Fe and impurities caused by smelting as the balance.

[0019] If particularly high demands are made on the supporting part regarding hardness, alternating bending strength and weldability with the working area, it can be advantageous for the supporting part to be made of a maraging steel consisting essentially of, in % by weight,

[0020] Mo 2.0 to 8.2

[0021] Ni 14.0 to 22.0

[0022] Co 5.0 to 14.0

[0023] Ti 0.2 to 1.7

[0024] Al 0.05 to 0.2

[0025] the balance being Fe and impurities caused by smelting.

[0026] With the above material for the support, as it has turned out, the welding seam is hard and tenacious over the entire cross section; no brittle phases have been detected and a particularly favorable heat treatment technology can be used that is adjustable to both tool parts.

[0027] If furthermore the metallic connection between the supporting part and the working part is made in a favorable manner by electron, laser or plasma welding, the material properties can be improved transversely over the connection zone and can feature high values.

[0028] In terms of manufacturing, but also with regard to an increased material quality and suitability for heat treatment, it may be preferred for the working part(s) to be made by powder metallurgy.

[0029] If, as can further be provided according to the invention, the working part(s) feature(s) granular or spherical hard material phases, it is possible to increase the service life of the tools for certain demands. However, proportions of hard material of more than 10% by volume in the working part cause it to become brittle.

[0030] The invention will be described in more detail with reference to an example.

[0031] A bandsaw having a thickness of 1.2 mm was made by welding a working part onto a supporting part by laser welding. The supporting part had a chemical composition in % weight of essentially 0.43 C, 0.75 Si, 0.9 Mn, 1.2 Cr, the balance being iron and impurities caused by manufacture. The working part had a material composition in % by weight of 0.06 C, 20.1 Co, 15.3 W, 2.2 Mo, 0.31 Si, 0.38 V, the balance being iron and impurities. The material for the support was manufactured by powder metallurgy using metal atomization with nitrogen, hot isostatic pressing and hot forming of the blank.

[0032] Tooth spaces were made in the bimetal strip such that the tooth tip areas were formed out of the working part.

[0033] A solution annealing of the working part was carried out at 1220 to 1270° C., the hardening of the cutting material was conducted at 580 to 650° C., whereby a material hardness of 67 to 68 HRC was achieved.

[0034] In practical use, when cutting 18/10 CrNi rods with a diameter of 210 mm, the saw according to the invention afforded a cutting time reduction of 53%. 

1. Composite tool consisting of a metallic supporting part and at least one such working part of different material compositions, which parts are metallically joined together, in particular a saw blade or a bandsaw, characterized in that the supporting part or the supporting strip is made of a tenacious iron-based material and the working part(s) are made of a precipitation hardenable iron-cobalt-tungsten alloy (Fe—Co—W).
 2. Composite tool according to claim 1, characterized in that the working part(s) has a composition in % by weight of Cobalt (Co) 15 to 30 Tungsten (W) up to 25 Molybdenum (Mo) up to 20 (W + Mo) 10 to 25 Silicon (Si) up to 1.5 Aluminum (Al) up to 1.5 Vanadium (V) up to 1.5 Titanium (Ti) up to 1.0 Niobium/Tantalum (Nb, Ta) up to 1.1 Carbon (C) a max. of 0.4 Chromium (Cr) a max. of 3.9 Nickel (Ni) a max. of 3.9 Manganese (Mn) a max of 4.1

the balance being iron (Fe) and impurities caused by production.
 3. Composite tool according to claim 1 or 2, characterized in that the working part(s) has a composition, in % by weight, of Co 22 to 26, preferably 21 to 24 W up to 20, preferably 9 to 18 Mo up to 12, preferably 1 to 9 (W + Mo) 11 to 20 Si up to 0.8, preferably up to 0.6 Al up to 0.8, preferably up to 0.4 V up to 1.0, preferably 0.4 to 0.8 Ti up to 0.6, preferably up to 0.3 Nb/Ta up to 0.7, preferably up to 0.25 C a max. of 0.2, preferably a max. of 0.15 Cr a max. of 0.9, preferably a max. of 0.5 Ni a max. of 0.8, preferably a max. of 0.3 Mn a max. of 0.9, preferably a max. of 0.4

the balance being Fe and impurities caused by manufacture.
 4. Composite tool according to any one of claims 1 to 3, characterized in that the supporting part is made of a carbon spring steel consisting of, in % by weight, 0.25 to 1.15 C 0.20 to 3.0 Si 0.45 to 2.5 Mn as well as Cr, V, Mo, Ni and S, Fe and impurities caused by smelting as the balance.
 5. Composite tool according to any one of claims 1 to 3, characterized in that the supporting part is made of a maraging steel consisting essentially of, in % by weight, Mo 2.0 to 8.2 Ni 14.0 to 22.0 Co 5.0 to 14.0 Ti 0.2 to 1.7 Al 0.05 to 0.2 the balance being Fe and impurities caused by smelting.
 6. Composite tool according to any one of claims 1 to 5, characterized in that the metallic bond between supporting part and working part is made by electron beam, laser or plasma welding.
 7. Composite tool according to any one of claims 1 to 6, characterized in that the working part(s) is (are) made by powder metallurgy.
 8. Composite tool according to any one of claims 1 to 7, characterized in that the working part(s) feature granular or spherical hard material phases up to a proportion of 10% by volume.
 9. Use of a tool according to the preceding claims for cutting austenitic steels and alloys. 